Polymer processing additives (PPA)

PPA HD-230 is a free flow, 25 mesh white powder fluoropolymer based processing additives. At a very low level addition (50-800 ppm), it can improve PE processing and does not affect the original physical property of the plastics as well as sealing, adhesion and printing. It can be used for LLDPE, HDPE, LDPE, EVA and other polyolefin resin.

Plasticisers

Light Stabilisers HALS UVA

HALS-944 is a polymerized highly effective HALS with low votality and low degredation, a fine heat stabilizer and anti-oxidant, working well with AO and UVA. It is widely used in polyolefin (such as PP, PE, HDPE, LDPE, LLDPE), PEX, co-polymers, soft and hard PVC, PVC blend and adherents.

Biocides

Filler Masterbatch

Filler	Physical properties	Features	Applications	Processing suggestion
CaCO3	Carrier: PE Powder size: D98 = 10 micron MFI: 4 g/10mins Density: 1.697 g/cm3 Moisture: 0.1% max	Grayish white powder. It can be mixed with polyethylene resin for film blowing, casting, injection, extrusion, etc. and is easy to disperse with good compatibility. It functions as a modifier to improve the heat resistance, slip resistance, size stability and printability. It also reduces heat release from burning and therefore prevents further environmental pollution.	PE roll bag PE film for food packaging HDPE container	General loading is recommended at 30%-50% with variation according to the products. The processing temperature is set according to resin’s processing temperature and it applies well among 220±40°C.
BaSO4	Carrier: PE Powder size: 5000 mesh MFI: 5 g/10mins Moisture: 0.01% max	Polypropylene based master batch containing 80%BASO4 powder. It is grayish white with excellent disersibility. It can be mixed with polyethylene resin for film blowing, casting, injection, extrusion etc. and is easy to disperse with good compatibility. It functions as a modifier to improve the heat resistance, slip resistance, size stability and printability. It also reduces heat release from burning and therefore prevents further environmental pollution.	PE shopping bag PE/PP pipe PP injection molding	General loading is recommended at 10%-30% with variation according to the products. The processing temperature is set according to resin’s processing temperature and it applies well among 220±40°C.
CaO desiccant	Carrier: Virgin LDPE Powder size: 8000 mesh MFI: 17 g/10mins Density: 1.4 g/cm3 Moisture: 0.01% max	Containing 50% CaO and 50% LDPE. It is white granule with good dispersibility.	Can be used in HDPE, LDPE, LLDPE, EVA,PP,PE,PS,HIPS, regeneration plastic etc. Suitable for blow film, plastic piece, plastic pipe, blow molding, coating film and injecting molding, thin film, tableware, plank, sheet, tubes, extrusion, and flow delay, etc.	Dosage rate: In the film, our suggestion additive rate is 1%-3%; In the plastic sheet, pipe, blow molding and injection products, our suggestion additive rate is 2%-5%; The ideal additive rate will be confirmed after testing.